Home > Products > ZIRCON SAND
ZIRCON SAND
|
Chemical composition
|
Standards for zircon sand products |
||||||
|
|
Advanced sand |
Super |
Grade 1 |
Grade 2 |
Grade 3 |
Grade 4 |
Grade 5 |
|
(Zr.Hr)O2 |
≥66.00 |
≥65.00 |
≥65.00 |
≥65.00 |
≥63.00 |
≥60.00 |
≥55.00 |
|
TiO2 |
≤0.08 |
≤0.15 |
≤0.50 |
≤1.00 |
≤2.50 |
≤3.50 |
≤8.00 |
|
Fe2O3 |
≤0.06 |
≤0.10 |
≤0.25 |
≤0.30 |
≤0.50 |
≤0.80 |
≤1.50 |
|
P2O3 |
|
≤0.20 |
≤0.25 |
≤0.35 |
≤0.50 |
≤0.80 |
≤1.50 |
|
Al2O3 |
|
≤0.80 |
≤0.80 |
≤0.80 |
≤1.00 |
≤1.20 |
≤1.50 |
|
SiO2 |
≤32.00 |
≤32.00 |
≤34.00 |
≤34.00 |
≤33.00 |
≤32.00 |
≤31.00 |
- Email:henryhnsc@126.com
- Tel: 8615890627213
- PRODUCTS
- WHITE FUSED ALUMINA
- BROWN FUSED ALUMINA
- SILICON CARBIDE
- CHROMITE SAND
- CERAMIC SAND
- GARNET SAND
- TABULAR ALUMINA
- BLACK FUSED ALUMINA
- ZIRCONIA FUSED ALUMINA
- GLASS BEADS
- BORON CARBIDE
- OTHER
- PRECIPITATED SILICA
- ZIRCON SAND
- IRON POWDER
hot PRODUCT
CONTACT US
Properties
Zircon sand, also known as zircon sand and zircon, is a mineral composed mainly of zirconium silicate (ZrSiO4). Pure zircon sand is a colorless transparent crystal.
Zircon is widely used in the foundry industry, mostly in the form of SAND and FLOUR (milled sand) for casting and refractory applications. Zircon’s properties make it ideal as a moulding base material for sand casting and investment casting, in addition to use as mould coating in die casting and in refractory paints and washes to reduce the wettability of other foundry sands.
Application
1, Refractory raw materials: used for the production of zirconium brick, zirconium jade fused brick, sintered brick, water brick, glass kiln zirconium ramming material, castable.
2, Ceramics: stable chemical performance, is a kind of high quality, cheap opacification agent, is widely used in all kinds of building ceramics, sanitary ceramics, daily ceramics, first-class handicraft ceramics production, in the processing and production of ceramic glaze, a wide range of use, large dosage.
3, Glass: television industry color picture tube, glass industry emulsion glass.
4. Coating: good suspension stability, excellent thixotropy and fluidity, good brushing, brushless coating, low organic content, small gas production, high coating strength.
5, Casting: with good thermal conductivity, small thermal expansion, thermal shock stability, high refractoriness, zirconium sand heat storage coefficient is also large. It has a strong cooling effect on castings, which can refine metal structure and improve mechanical properties.
|
Chemical composition
|
Standards for zircon sand products |
||||||
|
Advanced sand |
Super |
Grade 1 |
Grade 2 |
Grade 3 |
Grade 4 |
Grade 5 |
|
|
(Zr.Hr)O2 |
≥66.00 |
≥65.00 |
≥65.00 |
≥65.00 |
≥63.00 |
≥60.00 |
≥55.00 |
|
TiO2 |
≤0.08 |
≤0.15 |
≤0.50 |
≤1.00 |
≤2.50 |
≤3.50 |
≤8.00 |
|
Fe2O3 |
≤0.06 |
≤0.10 |
≤0.25 |
≤0.30 |
≤0.50 |
≤0.80 |
≤1.50 |
|
P2O3 |
|
≤0.20 |
≤0.25 |
≤0.35 |
≤0.50 |
≤0.80 |
≤1.50 |
|
Al2O3 |
|
≤0.80 |
≤0.80 |
≤0.80 |
≤1.00 |
≤1.20 |
≤1.50 |
|
SiO2 |
≤32.00 |
≤32.00 |
≤34.00 |
≤34.00 |
≤33.00 |
≤32.00 |
≤31.00 |
|
Refractive index |
1.93 to 2.01 |
|
Color |
Yellow white |
|
Specific Gravity |
4.6-4.71g/cm3 |
|
Bulk density |
2.6-2.8g/cm3 |
|
Mohs Hardness |
7.5 |
|
Thermal expansion coefficient |
0.003 cm/cm· ℃ |
|
Coefficient of Linear Expansion |
7.2x 10-6 cm/cm℃ |
|
Melting point |
2100-2300℃ |
|
PH |
6.0-8.5 |